Propylene Polymers Compositions

ABSTRACT

A propylene composition comprising (percent by weight): 
     A) 60%-95%, of a crystalline propylene copolymer containing from 2.0% to 10.0% of ethylene derived units having a melting point ranging from 148° C. to 160° C.; wherein the melting temperature Tm is measured by DSC on the as-reactor polymer; 
     B) 40%-5%, of a copolymer of ethylene containing from 70% to 85%, of ethylene derived units intrinsic viscosity ranging from 0.8 to 3 dl/g.

This application is the U.S. national phase of International Application PCT/EP2010/064736, filed Oct. 4, 2010, claiming priority to European Application 09172881.6 filed Oct. 13, 2009, and the benefit under 35 U.S.C. 119(e) of U.S. Provisional Application No. 61/279,591, filed Oct. 23, 2009; the disclosures of International Application PCT/EP2010/064736, European Application 09172881.6 and U.S. Provisional Application No. 61/279,591, each as filed, are incorporated herein by reference.

The present invention relates to a propylene polymer composition having an optimum balance of properties in particular improved impact strength and excellent optical properties. As is known, the isotactic polypropylene is endowed with an exceptional combination of excellent properties which render it suitable for a very great number of uses. In order to improve said properties into the propylene stereoregular homopolymerization process have been introduced one or more copolymerization steps or one or more monomer have been introduced in the homopolymer matrix.

WO 2006/037705 relates to an olefin polymer composition comprising (by weight, unless otherwise specified):

A) 60-85%, preferably 65-80%, more preferably 65-75%, of a crystalline propylene homopolymer or a crystalline copolymer of propylene containing 3% or less of ethylene or C₄-C₁₀ a-olefin(s) or of combinations thereof, said homopolymer or copolymer having a Polydispersity Index (P.I.) value of from 4.5-6, preferably 4.5-5.5, and a content of isotactic pentads (mmmm), measured by ¹³C NMR on the fraction insoluble in xylene at 25° C., higher than 96%, preferably higher than 98%;

B) 15-40%, preferably 20-35%, more preferably 25-35%, of a partially amorphous copolymer of ethylene containing from 35% to 70%, preferably from 40 to 55%, of propylene or C₄-C₁₀ a-olefin(s) or of combinations thereof, and optionally minor proportions of a diene. The olefin polymer composition exhibits a value of elongation at break ranging from 150 to 600%, preferably 200-500%, according to ISO method 527.

EP 603 723 relates to a polypropylene compositions comprising:

A) from 70 to 98 parts by weight of a crystalline propylene homopolymer, or a crystalline random copolymer of propylene with ethylene and/or C₄-C₁₀ alpha-olefins, containing from 0.5 to 10% by weight of ethylene and/or a-olefins (Fraction A); and

B) from 2 to 30 parts by weight of elastomeric copolymer of ethylene with one or more C₄-C₁₀ a-olefins, containing from 60 to 85% by weight of ethylene, and partially soluble in xylene at 25° C. (Fraction B);

Wherein said composition has an intrinsic viscosity value in tetrahydronaphthalene at 135° C. of the fraction soluble in xylene at 25° C. ranging from 0.8 to 1.1 dl/g.

The applicant found that the properties of these compositions, especially in terms of impact and transparency, can be improved by using a polypropylene matrix (polymer A) having a particular balance between melting point and ethylene content.

The object of the present invention is a propylene composition comprising (percent by weight):

A) 60%-95%, preferably 65%-90%, more preferably 70%-88%, of a propylene copolymer containing from 2.0% to 10.0% preferably from 3.0% to 6.0% more preferably from 3.1% to 6.0% of ethylene derived units having a melting temperature Tm ranging from 148° C. to 160° C. preferably from 149° C. to 160° C., preferably from 149° C. to 158° C., more preferably from 150° C. to 156° C.;

the Tm values characterizing the propylene polymers of the invention have to be measured on the “as-reactor polymer”, i.e. on the polymer as such without adding any additive or filler, in particular without adding nucleating agents.

B) 5%-40%, preferably 10%-35%, more preferably 12%-30% of a copolymer of ethylene with from 60% to 85%, preferably from 70% to 85%, more preferably from 71% to 82%; even more preferably from 71% to 81% of ethylene derived units, and having an intrinsic viscosity ranging from 0.8 to 3 dl/g preferably from 0.9 to 2.5 dl/g more preferably from 1 to 2 dl/g. From the above definitions it is evident that the term “copolymer” includes polymers containing only two kinds of comonomers.

Preferably in the propylene copolymer A) the ethylene content (C2) and the melting point (Tm) fulfil the following relationship:

Tm>C2*−0.56+150.5

preferably the relationship is

Tm>C2*−0.56+150.8

Even more preferably the relationship is:

Tm>C2*−0.56+151.2

Other preferred features for the compositions of the present invention are:

crystallization temperature Tc ranging from 95° C. to 120° C.;

MFR L (Melt Flow Rate according to ASTM 1238, condition L, i.e. 230° C. and 2.16 kg load) from 0.5 to 50 10 g/10 min, in particular from 9 to 30 g/10 min.; more preferably more preferably from 15 to 25 10 g/10 min;

Intrinsic Viscosity [I.V.] of the fraction (of the overall composition) soluble in xylene at room temperature: from 1.2 to 4.5, more preferably from 1.2. to 3 dl/g; even more preferably from 1.2 to 2 dl/g;

Moreover, the compositions of the present invention preferably are endowed with some or all these properties:

Haze measured on 1 mm plaques lower than 30%; preferably lower than 25%; even more preferably lower than 20%;

Izod impact strength measured at 23° C. higher than 4 KJ/m²;

ductile brittle temperature lower than +5° C., preferably lower than −3° C., more preferably lower than −6° C., even more preferably lower than −14° C., even more preferably lower than −19° C.

The propylene polymer compositions of the present invention can be prepared by sequential polymerization in at least two stages, with each subsequent polymerization stage being conducted in the presence of the polymeric material formed in the immediately preceding polymerization reaction, wherein the copolymer (A) is normally prepared in at least one first polymerization stage and the copolymer (B) is normally prepared in at least one second polymerization stage.

Preferably, each polymerization stage is carried out in presence of a highly stereospecific heterogeneous Ziegler-Natta catalyst. The Ziegler-Natta catalysts suitable for producing the propylene polymer compositions of the invention comprise a solid catalyst component comprising at least one titanium compound having at least one titanium-halogen bond and at least an electron-donor compound (internal donor), both supported on magnesium chloride. The Ziegler-Natta catalysts systems further comprise an organo-aluminum compound as essential cocatalyst and optionally an external electron-donor compound.

Suitable catalysts systems are described in the European patents EP45977, EP361494, EP728769, EP 1272533 and in the international patent application W000163261.

Preferably, the solid catalyst component comprises Mg, Ti, halogen and an electron donor selected from succinates of formula (I):

wherein the radicals R¹ and R², equal to or different from each other, are a C₁-C₂₀ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms belonging to groups 15-17 of the periodic table; the radicals R³ to R⁶ equal to or different from each other, are hydrogen or a C₁-C₂ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms, and the radicals R³ to R⁶ which are joined to the same carbon atom can be linked together to form a cycle.

R¹ and R² are preferably C₁-C₈ alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl groups.

Particularly preferred are the compounds in which R¹ and R² are selected from primary alkyls and in particular branched primary alkyls. Examples of suitable R¹ and R² groups are methyl, ethyl, n-propyl, n-butyl, isobutyl, neopentyl, 2-ethylhexyl. Particularly preferred are ethyl, isobutyl, and neopentyl.

One of the preferred groups of compounds described by the formula (I) is that in which R³ to R⁵ are hydrogen and R⁶ is a branched alkyl, cycloalkyl, aryl, arylalkyl and alkylaryl radical having from 3 to 10 carbon atoms. Another preferred group of compounds within those of formula (I) is that in which at least two radicals from R³ to R⁶ are different from hydrogen and are selected from C₁-C₂₀ linear or branched alkyl, alkenyl, cycloalkyl, aryl, arylalkyl or alkylaryl group, optionally containing heteroatoms belonging to groups.

Particularly preferred are the compounds in which the two radicals different from hydrogen are linked to the same carbon atom. Furthermore, also the compounds in which at least two radicals different from hydrogen are linked to different carbon atoms, that is R³ and R⁵ or R⁴ and R⁶ are particularly preferred.

According to a preferred method, the solid catalyst component can be prepared by reacting a titanium compound of formula Ti(OR)_(n−y)X_(y) where n is the valence of titanium and y is a number between 1 and n, preferably TiC4, with a magnesium chloride deriving from an adduct of formula MgCl₂·pROH, where p is a number between 0.1 and 6, preferably from 2 to 3.5, and R is a hydrocarbon radical having 1-18 carbon atoms. The adduct can be suitably prepared in spherical form by mixing alcohol and magnesium chloride in the presence of an inert hydrocarbon immiscible with the adduct, operating under stirring conditions at the melting temperature of the adduct (100-130° C.). Then, the emulsion is quickly quenched, thereby causing the solidification of the adduct in form of spherical particles. Examples of spherical adducts prepared according to this procedure are described in U.S. Pat. No. 4,399,054 and U.S. Pat. No. 4,469,648. The so obtained adduct can be directly reacted with the Ti compound or it can be previously subjected to thermal controlled dealcoholation (80-130° C.) so as to obtain an adduct in which the number of moles of alcohol is generally lower than 3, preferably between 0.1 and 2.5. The reaction with the Ti compound can be carried out by suspending the adduct (dealcoholated or as such) in cold TiCl₄ (generally 0° C.); the mixture is heated up to 80-130° C. and kept at this temperature for 0.5-2 hours. The treatment with Tic4 can be carried out one or more times. The internal donor can be added during the treatment with TiCl₄ and the treatment with the electron donor compound can be repeated one or more times. Generally, the succinate of formula (I) is used in molar ratio with respect to the MgC12 of from 0.01 to 1 preferably from 0.05 to 0.5. The preparation of catalyst components in spherical form is described for example in European patent application EP-A-395083 and in the International patent application W098144001. The solid catalyst components obtained according to the above method show a surface area (by B.E.T. method) generally between 20 and 500 m21g and preferably between 50 and 400 m21g, and a total porosity (by B.E.T. method) higher than 0.2 cm31g preferably between 0.2 and 0.6 cm31g. The porosity (Hg method) due to pores with radius up to 10.000 A generally ranges from 0.3 to 1.5 cm31g, preferably from 0.45 to 1 cm31g.

The organo-aluminum compound is preferably an alkyl-Al selected from the trialkyl aluminum compounds such as for example triethylaluminum, triisobutylaluminum, tri-n-butylaluminum, tri-n-hexylaluminum, tri-n-octylaluminum. It is also possible to use mixtures of trialkylaluminum's with alkylaluminum halides, alkylaluminum hydrides or alkylaluminum sesquichlorides such as AlEt₂Cl and Al₂Et₃Cl₃.

Preferred external electron-donor compounds include silicon compounds, ethers, esters such as ethyl 4-ethoxybenzoate, amines, heterocyclic compounds and particularly 2,2,6,6-tetramethyl piperidine, ketones and the 1,3-diethers. Another class of preferred external donor compounds is that of silicon compounds of formula R_(a) ⁵R_(b) ⁶Si(OR⁷)_(c) where a and b are integer from 0 to 2, c is an integer from 1 to 3 and the sum (a+b+c) is 4; R⁵, R⁶, and R⁷, are alkyl, cycloalkyl or aryl radicals with 1-18 carbon atoms optionally containing heteroatoms. Particularly preferred are methylcyclohexyldimethoxysilane, diphenyldimethoxysilane, methyl-t-butyldimethoxysilane, dicyclopentyldimethoxysilane, 2-ethylpiperidinyl-2-t-butyldimethoxysilane and 1,1,1, trifluoropropyl-2-ethylpiperidinyl-dimethoxysilane and 1,1,1, trifluoropropyl-metildimethoxysilane. The external electron donor compound is used in such an amount to give a molar ratio between the organo-aluminum compound and said electron donor compound of from 0.1 to 500.

The propylene copolymer A is obtainable by polymerizing propylene and ethylene by a gas-phase polymerization process carried out in at least two interconnected polymerization zones, the process comprising feeding propylene and the at least one linear or branched alpha-olefin having 2 to 8 carbon atoms other than propylene to said polymerization zones in the presence of a highly stereospecific heterogeneous Ziegler-Natta catalyst system under reaction conditions and collecting the polymer product from said polymerization zones, in which process the growing polymer particles flow upward through one of said polymerization zones (riser) under fast fluidization conditions, leave said riser and enter another polymerization zone (downcomer) through which they flow downward under the action of gravity, leave said downcomer and are reintroduced into the riser, thus establishing a circulation of polymer between the riser and the downcomer, whereby means are provided which are capable of totally or partially preventing the gas mixture present in the riser from entering the downcomer and a gas and/or liquid mixture having a composition different from the gas mixture present in the riser is introduced into the downcomer, the process being further characterized in that:

the monomer feed ratio C₂ ⁻(C₂ ⁻+C₃ ⁻) to the riser ranges from 0.020 to 1.000 mol/mol.

In the polymerization process, the growing polymer flows through a first polymerization zone, represented by the riser, under fast fluidization conditions. The two polymerization zones are appropriately interconnected. The growing polymer and the gaseous mixture leaving the riser are conveyed to a separation zone whereby the gaseous mixture is separated from the growing polymer. From the separation zone, the growing polymer enters the second polymerization zone, represented by the downcomer, where the growing polymer flows in a densified form under the action of gravity. The growing polymer particles leave said second polymerization zone and are reintroduced into said first polymerization zone, thus establishing a circulation of polymer between the two polymerization zones. The material balance is maintained by feeding in monomers and catalysts and discharging polymer powder. Generally, the conditions of fast fluidization in the first polymerization zone is established by feeding the monomers gas mixture below the point of reintroduction of the growing polymer into said first polymerization zone. The velocity of the transport gas injected into the riser has to be higher than the transport velocity under the operating conditions, and depends on the gas density and the particle size distribution of the solid. It is preferably comprised between 0.5 and 15 m/s, more preferably between 0.8 and 5 m/s. Generally, the various catalyst components are fed to the riser through a line that is preferably placed in the lower part of the riser. However, they can be fed at any other point of the riser, as well as at any point of the downcomer or of the interconnecting sections. The gas mixture that is separated from the circulating solid in the separation zone must be totally or partially prevented to enter the downcomer. This can be achieved by feeding a gas and/or liquid into the downcomer through a line placed at a suitable point of said downcomer, preferably in the upper part thereof, through one or more introduction lines. The gas and/or liquid mixture to be fed into the downcomer should have an appropriate composition, different from that of the gas mixture present in the riser. The said gas and/or liquid mixture partially or totally replaces the gas mixture entrained with the polymer particles entering the downcomer. The flow rate of this gas feed can be regulated so that a flow of gas counter-current to the flow of polymer particles is originated in the downcomer, particularly at the top thereof, thus acting as a barrier to the gas mixture coming from the riser which is entrained among the polymer particles. According to a particularly preferred embodiment, the gas and/or liquid mixture of different composition to be fed into the downcomer is fed in partially or totally liquefied form. More preferably, said gas and/or liquid mixture consists of liquefied propylene.

Optionally, one or more inert gases, such as nitrogen or an aliphatic hydrocarbon, are maintained in the polymerization zones, in such quantities that the sum of the partial pressures of the inert gases is preferably between 5 and 80% of the total pressure of the gases. The operating parameters such as, for example, the temperature are those that are usual in gas-phase olefin polymerization processes, for example between 50° C. and 120° C., preferably from 70° C. to 90° C. The process can be carried out under operating pressure of between 0,5 and 10 MPa, preferably between 1.5 and 6 MPa. The polymerization apparatus suitable for carrying out the process is described in details in the International Patent Application WO00/02929, in particular in FIG. 4. The molecular weight distribution of the growing polymers can be conveniently tailored by metering customary molecular weight regulators, particularly hydrogen, in different proportion into at least one polymerization zone, preferably into the riser. The process for the production of copolymer (A) is described in WO 2008/012144.

Polymer (B) is obtained by a polymerization in a gas phase in the presence of copolymer (A) without intermediate stages except for the partial degassing of the monomers. The reaction time, temperature and pressure of the polymerization steps are not critical, however the temperature for the preparation of fraction (A) and (B), that can be the same or different, is usually from 50° C. to 120° C. The polymerization pressure preferably ranges from 0.5 to 12 MPa if the polymerization is carried out in gas-phase. The catalytic system can be pre-contacted (pre-polymerized) with small amounts of olefins. The molecular weight of the propylene polymer composition is regulated by using known regulators, such as hydrogen.

In the second stage of the particularly preferred polymerization process, the ethylene/propylene copolymer (B) is produced in a conventional fluidized-bed gas-phase reactor in the presence of the polymeric material and the catalyst system coming from the preceding polymerization step. The polymerization mixture is discharged from the downcomer to a gas-solid separator, and subsequently fed to the fluidized-bed gas-phase reactor operating under conventional conditions of temperature and pressure.

The propylene polymer compositions of the present invention can also be obtained by separately preparing the said copolymers (A) and (B), operating with the same catalysts and substantially under the same polymerization conditions as previously illustrated and subsequently mechanically blending said copolymers in the molten state using conventional mixing apparatuses, like twin-screw extruders.

The propylene polymer compositions of the present invention may further comprise additives commonly employed in the polyolefin field, such as antioxidants, light stabilizers, nucleating agents, antiacids, colorants and fillers.

The main application of the propylene polymer compositions of the invention is the production of molded articles, particularly injection-molded items. The injection-molded articles comprising the propylene polymer compositions of the invention have good flexibility and good impact properties and are also endowed with good transparency.

The following examples are given to illustrate and not to limit the present invention.

EXAMPLES

The data of the propylene polymer materials were obtained according to the following methods:

Xylene-Soluble Faction

2.5 g of polymer and 250 rnL of o-xylene are introduced in a glass flask equipped with a refrigerator and a magnetical stirrer. The temperature is raised in 30 minutes up to the boiling pint of the solvent. The so obtained solution is then kept under reflux and stirring for further 30 minutes. The closed flask is then kept for 30 minutes in a bath of ice and water and in thermostatic water bath at 25 OC for 30 minutes as well. The solid thus obtained is filtered on quick filtering paper and the filtered liquid is divided into two 100 ml aliquots. One 100 ml aliquots of the filtered liquid is poured in a previously weighed aluminum container, which is heated on a heating plate under nitrogen flow, to remove the solvent by evaporation. The container is then kept on an oven at 80° C. under vacuum until constant weight is obtained. The residue is weighed to determine the percentage of xylene-soluble polymer.

Ethylene (C2) Content

By IR spectroscopy.

The comonomer content of the Component B is determined on the precipitated “amorphous” fraction of the polymer. The precipitated “amorphous” fraction is obtained as follows: to one 100 ml aliquot of the filtered liquid obtained as described above (procedure for the Xylene-soluble faction) 200 ml of acetone are added under vigorous stirring. Precipitation must be complete as evidenced by a clear solid-solution separation. The solid thus obtained is filtered on a tared metallic screen and dried in a vacuum oven at 70° C. until a constant weight is reached.

Molar Ratio Of Feed Gasses

Determined by gas-chromatography

Melt flow rate (MFR)

Determined according to ISO 1133 (230° C., 2.16 Kg)

Intrinsic Viscosity

Determined in tetrahydronaphthalene at 135° C.

Number Average Molecular Weight and Weight Average Molecular Weight

The determination of the molecular weights and the molecular weight distribution Mw/Mn was carried out by gel permeation chromatography (GPC) at 145° C. in 1,2,4-trichlorobenzene using a GPC apparatus model 150C from Waters. The data were evaluated by means of the Win-GPC software from HS-Entwicklungsgesellschaft fir wissenschaftliche Hard- and Software GmbH, Ober-Hilbersheim. The columns were calibrated by means of polypropylene standards having molecular weights from 100 to 107 g/mol.

Flexural Modulus

Determined according to ISO 178

Stress at Yield and at Break

Determined according to ISO 527

Elongation at Yield and Break

Determined according to ISO 527

IZOD Impact Strength

Determined according to ISO 18011A

Ductile/Brittle Transition Temperature (D/B)

According to this method, the bi-axial impact resistance is determined through impact with an automatic, computerized striking hammer.

The circular test specimens are obtained by cutting with circular hand punch (38 mm diameter). They are conditioned for at least 12 hours at 23° C. and 50 RH and then placed in a thermostatic bath at testing temperature for 1 hour. The force-time curve is detected during impact of a striking hammer (5.3 kg, hemispheric punch with a ½″ diameter) on a circular specimen resting on a ring support. The machine used is a CEAST 67581000 type model no. 2.

D/B transition temperature is the temperature at which 50% of the samples undergoes fragile break when submitted to the above-mentioned impact test. The plaques for DB measurements, having dimensions of 127×127×1.5 mm are prepared according to the following method.

The injection press is a Negri Bossi™ type (NB 90) with a clamping force of 90 tons. The mould is a rectangular plaque (127×127×1.5 mm).

The main process parameters are reported below:

Back pressure (bar): 20

Injection time (s): 3

Maximum Injection pressure (MPa): 14

Hydraulic injection pressure (MPa): 6−3

First holding hydraulic pressure (MPa): 4±2

First holding time (s): 3

Second holding hydraulic pressure (MPa): 3±2

Second holding time (s): 7

Cooling time (s): 20

Mould temperature (° C.): 60

The melt temperature is between 220 and 280° C.

Haze (on 1 mm Plaque)

According to the method used, 5×5 cm specimens are cut molded plaques of 1 mm thick and the haze value is measured using a Gardner photometric unit connected to a Hazemeter type UX-10 or an equivalent instrument having G.E. 1209 light source with filter “C”. Reference samples of known haze are used for calibrating the instrument. The plaques to be tested are produced according to the following method.

75×75×1 mm plaques are molded with a GBF Plastiniector G235190 Injection Molding Machine, 90 tons under the following processing conditions:

Screw rotation speed: 120 rpm

Back pressure: 10 bar

Melt temperature: 260° C.

Injection time: 5 sec

Switch to hold pressure: 50 bar

First stage hold pressure: 30 bar

Second stage pressure: 20 bar

Hold pressure profile: First stage 5 sec

Second stage 10 sec

Cooling time: 20 sec

Mold water temperature: 40° C.

Hexane Extractable

The hexane extractable fraction is determined according to modified FDA method (federal registration, title 21, Chapter 1, part 177, section 1520, s. Annex B) on polymer formed into 100 ym thick items.

Melting Temperature, Melting Enthalpy and Crystallization Temperature

Determined by differential scanning calorimetry (DSC). weighting 6±1 mg, is heated to 220±1° C. at a rate of 20° C./min and kept at 220±1° C. for 2 minutes in nitrogen stream and it is thereafter cooled at a rate of 20° C./min to 40±2° C., thereby kept at this temperature for 2 min to crystallise the sample. Then, the sample is again fused at a temperature rise rate of 20° C./min up to 220° C.±1. The melting scan is recorded, a thermogram is obtained, and, from this, melting temperatures and crystallization temperatures are read.

EXAMPLE 1 Polymerization Equipment

The propylene polymer compositions of the example were prepared in a two-step polymerization process, wherein the copolymer (A) was prepared in the first polymerization step by feeing the monomers and the catalyst system to a gas-phase polymerization reactor comprising two interconnected polymerization zones, a riser and a downcomer, as described in the European Patent EP782587. The polymerization mixture was discharged from said reactor, conveyed to a gas-solid separator and the polymerized material was sent into a conventional gas-phase fluidized-bed reactor where the ethylene/propylene copolymer (B) was produced. The operative conditions are indicated in Table 1.

Example 1

The solid catalyst used to prepare the propylene polymers was prepared according to the Example 5, lines 48-55 of the European Patent EP728769. Triethylaluminium (TEAL) was used as co-catalyst and dicyclopentyldimethoxysilane as external donor. The propylene polymers were prepared by feeding the monomers and the catalyst system to the polymerization equipment indicated above. The polymer powders were subjected to a steam treatment to remove the unreacted monomers, dried and subject to the analysis. and the results analysis of the obtained polymer are indicated in table 1.

On Table 2 are reported the characterization data measured on the compositions obtained by mixing the polymer powders of the Example 1 with 1800 ppm of Millad 3988 extruded in a twin-screw extruder Berstorff (L/D=33) under the following operating conditions:

Temperature of the feeding section: 190-210° C.

Melt temperature: 240° C.

Temperature of the die section: 230° C.

Flow rate: 16 Kg/h

Rotational speed: 250 rpm

TABLE 1 Example 1 Component A TEAL/external donor wt/wt 4 TEAL/catalyst wt/wt 5 Temperature ° C. 70 Pressure barg 24 Split holdup wt % 40 riser downcomer wt % 60 H2/C3 riser mol/mol 0.19 (riser)/ 0.076 (downer) C2/(C2 + C3) mol/mol 0.033 (riser)/ 0.005 (downer) MFR g/10 min 20 C2 total content wt % 3.2 XS wt % 6.1 Tm ° C. 150 Component B Temperature ° C. 80 Pressure MPa 2 Split % 15 C2/C2 + C3 0.8 H2/C2 0.47 C2 = ethylene C3 = propylene H2 = hydrogen XS = xylene solubles

The properties measured on the samples are collected in Table 2.

TABLE 2 Ex 1 Polymer A MFR g/10′ 20 C2 wt % 3.2 Melting point ° C. 153 XS wt % 6 Polymer B % split wt % 15 % C2 copolymer wt % 80 Composition XSIV Dl/g 1.2 Elongation at break % 420 Izod Impact 23° C. kJ/m2 6 D/B TT ° C. −19.7 Haze (1 mm plaque) % 16.4 XSIV = xylene soluble fraction C2 = ethylene 

1. A propylene composition comprising (percent by weight): A) 60%-95%, of a crystalline propylene copolymer containing from 2.0% to 10.0% of ethylene derived units having a melting point ranging from 148° C. to 160° C.; wherein the melting temperature Tm is measured by DSC on the as-reactor polymer; and B) 5%-40%, of a copolymer of ethylene containing from 70% to 85%, of ethylene derived units, wherein the propylene composition has an intrinsic viscosity ranging from 0.8 to 3 dl/g.
 2. The composition according to claim 1 wherein component A) is a propylene copolymer containing from 3.0% to 6.0% by weight of ethylene derived units and component B) is a copolymer of ethylene containing from 70% to 82%; by weight of propylene derived units.
 3. The composition according to claim 1 wherein the ethylene content (C2) and the melting point (Tm) of the component A) fulfil the following relationship: Tm>C2*−0.56+150.5.
 4. The composition according to claim 1 wherein component A) has a melting point ranging from 149° C. to 160° C.
 5. The composition according to claim 1 wherein the relationship between the ethylene derived units C2 content and the melting point Tm is Tm>C2*−0.56+150.8
 6. The composition according to claim 1 wherein the intrinsic Viscosity [I.V.] of the fraction (of the overall composition) soluble in xylene at room temperature is from 1.2 to 4.5.
 7. The composition according to claim 1 having a haze lower than 25%
 8. A thermoformed article comprising the propylene polymer composition of claim
 1. 